Waterborne polyurethane resin for wood lacquer and other hard coatings

Product name

JK-5202

JK-5203

JK-5204

JK-5205

JK-5206

JK-5207

Solid content(%)

30

35

35

35

45±2

45±2

Emulsion appearance

translucent

translucent

Translucent emulsion

Translucent white

Translucent milky white

Translucent milky white

Viscosity(CPS)

<500

<500

<500

<500

<1000

<1000

PH

7~8.5

7~8.5

7~8.5

7~8.5

7~7.5

7~7.5

100%Modulus

25±3

15±3

15±3

45±5

28±3

13±2

Tensile strength(Mpa)

>40

>30

>50

>55

>45

>45

Elongation(%)

>100

>200

>300

>250

>400

>400

Characteristic

1. Aliphatic

2. Hardness: 2H

3. Good compatibility with propylbenzene and pure propyl

4. Good adhesion to metal substrates

5. Good adhesion to chemical fiber

1. Aliphatic

2. Hardness: HB

3. Good adhesion to the substrate

4. High gloss

1. Aliphatic

2. Hard, alcohol resistant

3. High gloss

4. Wear and scratch resistance

5. The coating is thick and strong

1. Aliphatic

2. Hardness: 3H

3. High gloss

4. Wear-resistant, scratch-resistant

5. Salt spray resistance

1. Aliphatic

2. Hardness: 2.5H

3. Good adhesion to the substrate

4. Anti-high temperature back viscosity

5. Film-forming high-gloss transparent complete

1. Aliphatic

2. Hardness: 1.5H

3. Good adhesion to the substrate

4. Anti-high temperature back viscosity

5. Film-forming high-gloss transparent complete

Application range

1. Used in wood finish

2. As a composite fiber

1. Used in wood finish

2. High gloss coating ink

1. Printing ink for alcohol-resistant alcohol packaging box

2. Outdoor durable paint and ink

3. The basic resin for making wood lacquer

APEO formaldehyde content: 0 Plasticizer content: 0 Harmful eight heavy metals: 0